Efere ígwè

Ọ bụ nchara dị larịị nke a na-eji ígwè a wụrụ awụ awụ wee pịa ya ka ọ dị jụụ.
Ọ dị larịị, akụkụ anọ ma nwee ike ịkpụgharị ya ozugbo ma ọ bụ bepụ ya na ibe nchara sara mbara.
A na-ekewa efere ígwè ahụ dị ka ọkpụrụkpụ, efere ígwè dị mkpa bụ ihe na-erughị 4 mm (nke kachasị dị mkpa bụ 0.2 mm), efere ígwè na-acha uhie uhie bụ 4-60 mm, na efere ígwè ọzọ dị 60-115. mm.
A na-ekewa mpempe ígwè n'ime ọkụ na-ekpo ọkụ na oyi na-atụ dịka ntụgharị.
The obosara nke mkpa efere bụ 500 ~ 1500 mm; obosara nke oké mpempe akwụkwọ bụ 600 ~ 3000 mm. A na-ekewa akwụkwọ mpempe akwụkwọ site na ụdị ígwè, gụnyere ígwè nkịtị, ígwè dị elu, ígwè alloy, igwe mmiri mmiri, igwe anaghị agba nchara, ngwá ọrụ ígwè, ígwè na-eguzogide okpomọkụ, ígwè na-ebu ígwè, silicon ígwè na ụlọ ọrụ mmepụta ihe dị ọcha, wdg; Enamel efere, bulletproof efere, wdg Dị ka elu mkpuchi, e nwere galvanized mpempe akwụkwọ, tin-plated mpempe akwụkwọ, ndu-plated mpempe akwụkwọ, plastic mejupụtara efere ígwè, wdg.
Nchara nhazi ala dị ala
(nke a makwaara dị ka obere alloy steel nkịtị, HSLA)
1. Nzube
A na-ejikarị emepụta àkwà mmiri, ụgbọ mmiri, ụgbọ ala, ndị na-ekpo ọkụ ọkụ, ụgbọ mmiri dị elu, mmanụ na mmanụ gas, nnukwu ígwè ígwè, wdg.
2. Arụmọrụ chọrọ
(1) Ike dị elu: n'ozuzu ike mkpụrụ ya dị n'elu 300MPa.
(2) Ike siri ike: elongation chọrọ ka ọ bụrụ 15% ruo 20%, na mmetụta siri ike na ime ụlọ dị elu karịa 600kJ / m ruo 800kJ / m. Maka nnukwu akụrụngwa welded, a chọkwara nnukwu mgbaji siri ike.
(3) Ezi ịgbado ọkụ arụmọrụ na oyi akpụ arụmọrụ.
(4) Okpomọkụ mgbanwe oyi na-adịghị ala.
(5) Ezigbo nguzogide corrosion.
3. Ihe eji eme ihe
(1) Carbon dị ala: N'ihi nnukwu ihe achọrọ maka ịdị ike, weldability na ụdị oyi, ọdịnaya carbon anaghị agafe 0.20%.
(2) Tinye ihe ndị na-eme ka manganese dabere.
(3) Ịgbakwunye ihe inyeaka dị ka niobium, titanium ma ọ bụ vanadium: obere niobium, titanium ma ọ bụ vanadium na-emepụta ezigbo carbides ma ọ bụ carbonitrides na ígwè, nke bara uru iji nweta ezigbo ọka ferrite ma melite ike na ike nke ígwè.
Na mgbakwunye, ịgbakwụnye obere ọla kọpa (≤0.4%) na phosphorus (ihe dị ka 0.1%) nwere ike imeziwanye nguzogide corrosion. Ịgbakwunye obere ihe nke ụwa na-adịghị ahụkebe nwere ike imebi na degas, mee ka ígwè dị ọcha, ma melite ike na nhazi ọrụ.
4. A na-ejikarị ígwè arụ ọrụ ala alloy dị ala
16Mn bụ ụdị ígwè dị ike dị ala na-arụ ọrụ nke ọma na obodo m. Ọdịdị a na-eji steeti bụ ferrite-pearlite dị mma, ike ya dịkwa ihe dịka 20% ruo 30% dị elu karịa nke ígwè arụ ọrụ carbon nkịtị Q235, na nguzogide corrosion ikuku ya dị 20% ruo 38% elu.
15MnVN bụ igwe a na-ejikarị eme ihe na nchara siri ike. Ọ nwere ike dị elu, yana ịdị mma dị mma, weldability na obere okpomọkụ siri ike, a na-ejikwa ya na-emepụta nnukwu ihe owuwu dị ka àkwà mmiri, mmiri ọkụ, na ụgbọ mmiri.
Mgbe ọkwa ike gafere 500MPa, ihe owuwu ferrite na pearlite siri ike imezu ihe ndị a chọrọ, ya mere a na-emepụta nchara carbon bainitic dị ala. Mgbakwunye nke Cr, Mo, Mn, B na ihe ndị ọzọ bara uru iji nweta usoro bainite n'okpuru ọnọdụ ikuku jụrụ oyi, nke mere na ike dị elu, plasticity na ịgbado ọkụ na-arụ ọrụ dịkwa mma, a na-ejikarị ya na ndị na-ekpo ọkụ ọkụ. , ụgbọ mmiri dị elu, wdg.
5. Njirimara ọgwụgwọ okpomọkụ
A na-ejikarị ụdị ígwè a eme ihe na ọnọdụ okpomọkụ na-ekpo ọkụ na ikuku na-adịghị achọ ọgwụgwọ okpomọkụ pụrụ iche. Ihe microstructure na-eji steeti na-abụkarị ferrite + sorbite.
Alloy carburized ígwè
1. Nzube
A na-eji ya eme ihe n'ịmepụta ngwa nnyefe n'ime ụgbọ ala na traktọ, camshafts, piston pin na akụkụ igwe ndị ọzọ n'ime engine combustion. Akụkụ ndị dị otú ahụ na-ata ahụhụ site na esemokwu siri ike ma na-eyi n'oge ọrụ, ma n'otu oge ahụ na-ebu ibu na-agbanwe agbanwe, karịsịa na-emetụta ibu.
2. Arụmọrụ chọrọ
(1) N'elu carburized oyi akwa nwere nnukwu ike siri ike iji hụ na nkwụsi ike na-eyi nke ọma na kọntaktị ike ọgwụgwụ, yana plasticity kwesịrị ekwesị na ike siri ike.
(2) Isi nwere nnukwu ike na ike zuru oke. Mgbe ike nke isi adịghị ezughi oke, ọ dị mfe imebi n'okpuru ọrụ mmetụta ma ọ bụ ibu ibu; mgbe ike na-ezughị ezu, a na-agbaji oyi akwa carburized na-agbaji ngwa ngwa ma kpochapụ ya.
(3) Ezi okpomọkụ ọgwụgwọ usoro arụmọrụ N'okpuru elu carburizing okpomọkụ (900 ℃～950 ℃), na austenite grains adịghị mfe na-eto eto na nwere ezi hardenability.
3. Ihe eji eme ihe
(1) Carbon dị ala: ọdịnaya carbon bụ n'ozuzu 0.10% ruo 0.25%, nke mere na isi akụkụ ahụ nwere plastik zuru oke na ike.
(2) Tinye ihe alloying iji kwalite ike ike: Cr, Ni, Mn, B, wdg. na-agbakwunyekarị.
(3) Tinye ihe ndị na-egbochi uto nke ọka austenite: tumadi tinye obere ego nke carbide siri ike na-emepụta ihe Ti, V, W, Mo, wdg iji mee ka carbide alloy kwụsie ike.
4. Steel ọkwa na ọkwa
20Cr ala hardenability alloy carburized ígwè. Ụdị ígwè a nwere ike siri ike na ike dị ala.
20CrMnTi ọkara hardenability alloy carburized ígwè. Ụdị nchara a nwere ikike siri ike dị elu, mmetụta na-ekpo ọkụ na-ekpo ọkụ dị ala, oyi akwa mgbanwe carburizing na-agbanwe agbanwe, yana ezigbo ígwè ọrụ na nkà na ụzụ.
18Cr2Ni4WA na 20Cr2Ni4A elu hardenability alloy carburized ígwè. Ụdị nchara a nwere ihe ndị ọzọ dị ka Cr na Ni, nwere ike siri ike, ma nwee mmetụta siri ike dị mma na obere okpomọkụ mmetụta siri ike.
5. Okpomọkụ ọgwụgwọ na microstructure Njirimara
Usoro ọgwụgwọ okpomọkụ nke alloy carburized ígwè bụ n'ozuzu kpọmkwem quenching mgbe carburizing, na mgbe ahụ tempering na ala okpomọkụ. Mgbe ọgwụgwọ okpomọkụ gasịrị, usoro nke elu carburized oyi akwa bụ alloy cementite + tempered martensite + obere ego nke austenite ejigidere, na ike bụ 60HRC ~ 62HRC. Ihe owuwu bụ isi metụtara ike siri ike nke ígwè na oke akụkụ nke akụkụ ahụ. Mgbe agbasiri ike nke ọma, ọ bụ martensite nwere obere carbon nwere ike nke 40HRC ruo 48HRC; n'ọtụtụ ọnọdụ, ọ bụ troostite, martensite na-ekpo ọkụ na obere ígwè. Element ahu, ike bụ 25HRC ~ 40HRC. Isi ike nke obi na-adịkarị elu karịa 700KJ/m2.
Alloy menyụọ na nchara nchara
1. Nzube
Alloy quenched na tempered nchara na-ọtụtụ ebe na-emepụta nke dị iche iche dị mkpa akụkụ na ụgbọala, traktọ, igwe ngwaọrụ na ndị ọzọ igwe, dị ka gia, aro, njikọ mkpara, bolts, wdg.
2. Arụmọrụ chọrọ
Ọtụtụ n'ime akụkụ ndị na-emenyụ ọkụ na ndị na-ekpo ọkụ na-ebu ibu dị iche iche na-arụ ọrụ, ọnọdụ nrụgide dị mgbagwoju anya, na ihe ndị dị elu na-arụ ọrụ dị elu chọrọ, ya bụ, ike dị elu na ezigbo plasticity na siri ike. Alloy menyụọ na igwe ọkụ na-achọkwa ike siri ike. Otú ọ dị, ọnọdụ nrụgide nke akụkụ dị iche iche dị iche iche, ihe ndị a chọrọ maka ike siri ike dị iche iche.
3. Ihe eji eme ihe
(1) Carbon dị ala: ọdịnaya carbon na-adịkarị n'etiti 0.25% na 0.50%, yana 0.4% n'ọtụtụ;
(2) Na-agbakwụnye ihe Cr, Mn, Ni, Si, wdg iji melite hardability: Na mgbakwunye na imeziwanye ike, ihe ndị a alloy nwekwara ike ịmepụta alloy ferrite ma melite ike nke ígwè. Dịka ọmụmaatụ, arụmọrụ nke 40Cr ígwè mgbe emechara na ọgwụgwọ tempering dị elu karịa nke ígwè 45;
(3) Tinye ihe iji gbochie ụdị nke abụọ nke iwe ọkụ: alloy quenched na tempered steel nwere Ni, Cr, na Mn, nke na-adịkarị n'ụdị nke abụọ nke iwe ọkụ n'oge okpomọkụ dị elu na ngwa ngwa jụrụ oyi. Ịtinye Mo na W na ígwè nwere ike igbochi ụdị nke abụọ nke iwe ọkụ, na ọdịnaya kwesịrị ekwesị bụ ihe dịka 0.15% -0.30% Mo ma ọ bụ 0.8% -1.2% W.
Ntụle nke akụrụngwa nke 45 ígwè na 40Cr ígwè mgbe quenching na tempering
Ọkwa igwe na ọnọdụ ọgwụgwọ okpomọkụ Nkebi nkebi / mm sb/ MPa ss/MPa d5/% y/% ak/kJ/m2
45 ígwè 850 ℃ mmiri quenching, 550 ℃ tempering f50 700 500 15 45 700
40Cr ígwè 850 ℃ mmanụ quenching, 570 ℃ tempering f50 (isi) 850 670 16 58 1000
4. Steel ọkwa na ọkwa
(1) 40Cr ala hardenability quenched na tempered ígwè: The oké egwu dayameta nke mmanụ quenching nke ụdị ígwè bụ 30mm ka 40mm, nke a na-eji na-emepụta akụkụ dị mkpa nke izugbe size.
(2) 35CrMo ọkara hardenability alloy quenched na tempered ígwè: dayameta dị oke egwu nke mmanụ quenching nke ụdị ígwè bụ 40mm ka 60mm. Mgbakwunye nke molybdenum nwere ike ọ bụghị naanị imeziwanye ike, kamakwa igbochi ụdị nke abụọ nke iwe ọkụ.
(3) 40CrNiMo high hardenability alloy quenched na tempered ígwè: oké egwu dayameta nke mmanụ quenching nke ụdị ígwè bụ 60mm-100mm, ọtụtụ n'ime ha bụ chromium-nickel ígwè. Ịgbakwunye molybdenum kwesịrị ekwesị na chromium-nickel ígwè ọ bụghị nanị na ọ nwere ike siri ike, kamakwa ọ na-ewepụ ụdị nke abụọ nke iwe ọkụ.
5. Okpomọkụ ọgwụgwọ na microstructure Njirimara
Ọgwụgwọ okpomọkụ ikpeazụ nke alloy quenched na igwe na-ekpo ọkụ na-ekpo ọkụ na-ekpo ọkụ na okpomọkụ dị elu (quenching na tempering). Alloy quenched na tempered ígwè nwere nnukwu hardening, na mmanụ na-emekarị na-eji. Mgbe ike siri ike dị ukwuu, ọ nwere ike ọbụna mee ka ikuku dị jụụ, nke nwere ike ibelata ntụpọ ọgwụgwọ okpomọkụ.
Ngwongwo ikpeazụ nke alloy quenched na igwe na-ekpo ọkụ na-adabere na okpomọkụ dị ọkụ. N'ozuzu, tempering na 500 ℃-650 ℃ na-eji. Site na ịhọrọ ọnọdụ okpomọkụ, enwere ike nweta ihe ndị achọrọ. Iji gbochie ụdị nke abụọ nke iwe ọkụ, ngwa ngwa jụrụ oyi (mmiri jụrụ oyi ma ọ bụ mmanu mmanu) mgbe iwesasịrị na-aba uru maka mmelite nke ike.
The microstructure nke alloy quenched na tempered ígwè mgbe ot okpomọkụ ọgwụgwọ bụ tempered sorbite. Maka akụkụ ndị chọrọ elu na-eguzogide iyi (dị ka ngwo na spindles), a na-emenyụ ọkụ ọkụ ọkụ na-ekpo ọkụ na obere okpomọkụ, na nhazi elu na-ewe iwe martensite. Isi ike nke elu nwere ike iru 55HRC ~ 58HRC.
The mkpụrụ ike alloy quenched na tempered ígwè mgbe quenching na tempering bụ banyere 800MPa, na mmetụta siri ike bụ 800kJ / m2, na isi ike nke isi nwere ike iru 22HRC ~ 25HRC. Ọ bụrụ na akụkụ nke obe buru ibu ma ghara isi ike, arụ ọrụ ahụ na-ebelata nke ukwuu.